HGM-125 is a specially formulated non-shrink, high-strength grouting material designed for offshore wind turbine foundations, monopiles, jackets, and transition pieces. It offers exceptional performance in marine environments with superior bonding, early strength gain, long-term durability, and resistance to sulfate, chloride, and freeze-thaw cycles.
Keywords:
Offshore wind power grout
High strength non-shrink grout
Grout for wind turbine foundation
Product Introduction
HGM-125 Offshore wind power special high-strength non-shrinkage grouting material is a modified cement-based grouting material, developed using polymer and nano enhancement technology, the product has a large mobility, high early strength, ultra-high strength, super durability, non-shrinkage and high fatigue resistance.
1. High Early & Final Strength: >80 MPa compressive strength in 28 days.
2. Non-Shrink Formulation: No settlement or cracking after curing.
3. Marine Environment Resistant: Resists sulfate, chloride, and sea spray.
4. Excellent Bonding: Strong adhesion to concrete and steel.
5. Fast Curing: Supports fast installation of turbines.
6. Stable in Harsh Conditions: Works from -10°C to 50°C.
1.Offshore wind turbine foundations (monopile, jacket, tripod)
2.Heavy equipment baseplates in marine environments
3.Pile cap and socket connections under dynamic load
4.Offshore booster station conduit frame foundation grouting.
Q: Is HGM-125 suitable for underwater pouring?
A: Yes, it can be used in submerged conditions with anti-washout properties.
Q: Can it resist marine corrosion and salt spray?
A: Absolutely. It’s specially formulated for marine durability.
Q: How fast can structures be loaded after grouting?
A: Light loads can be applied after 24 hours; full design load typically after 7 days.
Product Parameters
| Property | Value |
| Appearance | Gray powder |
| Water-to-powder ratio | 0.12–0.14 |
| Working time | ~30 minutes |
| Initial setting time | ≤ 3 hours |
| Final setting time | ≤ 6 hours |
| 1-day compressive strength | ≥ 30 MPa |
| 28-day compressive strength | ≥ 80 MPa |
| Expansion rate | 0.02%–0.1% |
| Chloride ion content | < 0.03% |
| Shrinkage | None (non-shrink) |
Packed in kraft paper, 50kg/bag, pay attention to moisture-proof, shelf life is 6 months.
Hot Products
Silane impregnating agent-A surface applied, non-film forming protection siloxane based product which can improve the durability of concrete structure. We have four products with Isobutyltriethoxysilane, Isooctyltriethoxysilane, n-Butyltriethoxysilane, and n-Octyltriethoxysilane as the main component.
Anchoring of railway concrete sleepers with spikes, prefabricated bridge cementing joints, and anchoring of anchor bolts for mechanical equipment.
Premium carbon fiber grid fabric for concrete repair & structural reinforcement. corrosion-resistant, 5x lighter than steel mesh.
Underwater Epoxy Bonding Agent
Reinforcement and reconstruction of steel plates, carbon fiber cloth, or concrete components and masonry components with RH above 90%.
Elastic concrete is an elastic polymer material composed of component A, B, and C. Among them, components A and B are polymer elastic resin and toughening curing agent respectively, and component C is special aggregate.
Leikesitm-Copper-Plated Steel Fiber
Usage: Highway and bridge; Railway engineering; Pipeline engineering; Hydraulic dam; Port and ocean engineering
Start Enhancing Your Business With a Concrete Solution Today
Our products have undergone rigorous testing at our national testing laboratory (CABR testing center co., ltd). Renowned Fortune Global 500 firms such as China Railway Group Limited, China Communications Construction Company Limited, and Sinohydro are among our esteemed clients.
Navigation
Navigation
Contact Us
Get in Touch
Get in Touch